Pelletizing iron ore is undertaken due to the excellent physical and metallurgical properties of iron ore pellets.[1] Iron ore pellets are spheres of typically 6-16 mm (0.24-0.63 in) to be used as raw material for blast furnaces. They typically contain 64% Fe and various additional material adjusting the chemical composition and the metallurgical properties of the pellets.Typically limestone, dolomite and powder coal are added and Bentonite is used as binder.
The process of pelletizing combines mixing of the raw material, forming the pellet and a thermal treatment baking the soft raw pellet to hard spheres. The raw material is rolled into a ball, then fired in a kiln or in travelling grate to sinter the particles into a hard sphere.
The configuration of iron ore pellets as packed spheres in the blast furnace allows air to flow between the pellets, decreasing the resistance to the air that flows up through the layers of material during the smelting. The configuration of iron ore powder in a blast furnace is more tightly-packed and restricts the air flow. This is the reason that iron ore is preferred in the form of pellets rather than in the form of finer particles.[5] The quality of the iron ore pellets depends on different factors, which include feed particle size, amount of water used, disc rotating speed. inclination angle of the disc bottom, residence time in the disc as well as the quality and quantity of the binder(s) used.
Preparation of raw materials
Additional materials are added to the iron ore (pellet feed) to meet the requirements of the final pellets. This is done by placing the mixture in the pelletizer, which can hold different types of ores and additives, and mixing to adjust the chemical composition and the metallurgic properties of the pellets. In general, the following stages are included in this period of processing: concentration / separation, homogenization of the substance ratios, milling, classification, increasing thickness, homogenization of the pulp and filtering.
Formation of the raw Pellets
Disc Pelletizer
The formation of raw iron ore pellets, also known as pelletizing, has the objective of producing pellets in an appropriate band of sizes and with mechanical properties high usefulness during the stresses of transference, transport, and use. For example, waste materials are ground before being heated and introduced into a press for compression.[6] Both mechanical force and thermal processes are used to produce the correct pellet properties. From an equipment point of view there are two alternatives for industrial production of iron ore pellets: the drum and the pelletizing disk.
Thermal processing
In order to confer to the pellets high resistance metallurgic mechanics and appropriate characteristics, the pellets are subjected to thermal processing, which involves stages of drying, preheating, firing, after-firing and cooling. The duration of each stage and the temperature that the pellets are subjected to have a strong influence on the final product quality.
#pellet
#pelletindustry
#ironore
#subhajitmondal
#MPS
#meanparticlesize
#dri
#pelletizing
#pelletizingplant
#blastfurnace
#pelletsponge
Негізгі бет Ғылым және технология How to calculate Mean Particle Size(MPS) on Pellet material || Iron ore pellet size analysis ||
Пікірлер: 4