Thank you for your time making this excellent lecture! Please I am not a nitrider but I would like to try the salt bath nitride process on hot forging molds. I am unclear what salt bath is best for a deeper case but leaning toward a (Li-carbonate + K-cyanate + Cyanuric acid) bath. Please what bath composition would you recommend? (I would prefer to support a more environmentally friendly supplier but must be balanced with a good quality nitride). Thank you much. -John
@engineersarfrazahmed2609
3 жыл бұрын
Sir can you give salts composition for steel grade 1082 and heat resistant alloys
@johnmurphy5428
5 жыл бұрын
Added to previous comment: My molds are H13 @51HRC via vacuum hardening/2-bar quench with three tempers, the final tempering temperature @555'C. Thank you
Пікірлер: 5